Investigation of changing failure mechanisms in the VHCF regime caused by different strengths of a martensitic steel

  • The present study gives an overview of recent investigations dealing with the fatigue behaviour of the tempered martensitic steel 50CrMo4 (Fe-0.5wt%C-1wt%Cr) in the HCF and VHCF regime by taking into account a variation in material strength, by modifying the heat treatment parameters. The parameters for the tempering treatment were adapted to receive two material conditions with 37HRC and 57HRC, respectively. Subsequently, fatigue specimens were machined from the heat-treated bars for fatigue tests in an ultrasonic (f=20000Hz) and a resonance (f=95Hz) fatigue testing machine under fully reversed loading (R=-1) at laboratory air atmosphere. It was found that the dominant fatigue and fracture mechanisms change with increasing material strength. For 37HRC moderate-strength specimens crack initiation was shown to occur on the specimen surface within Cr depleted bands (segregation bands) as the dominant fatigue damage mechanism. Contrary to that, only internal crack initiation at non-metallic inclusions was observed for the high strength 57HRC condition. Furthermore, the completely different crack initiation mechanisms of the two heat treatment conditions were assessed by applying the Murakami approach relating the fatigue limit with the size of non-metallic inclusions.

Export metadata

Additional Services

Share in Twitter Search Google Scholar
Metadaten
Author:Alexander Giertler, Kevin Koschella, Ulrich Krupp
Title (English):Investigation of changing failure mechanisms in the VHCF regime caused by different strengths of a martensitic steel
URL:https://www.sciencedirect.com/science/article/pii/S2452321617304511
ISSN:2452-3216
Parent Title (English):Procedia Structural Integrity
Publisher:Elsevier
Place of publication:Amsterdam
Editor:Stefano Beretta
Document Type:Part of Periodical
Language:English
Year of Completion:2017
Release Date:2018/06/05
Tag:Materialermüdung
Volume:7
Pagenumber:6
First Page:321
Last Page:326
Faculties:Fakultät IuI
DDC classes:500 Naturwissenschaften und Mathematik
Review Status:Veröffentlichte Fassung/Verlagsversion