TY  - JOUR
U1  - Zeitschriftenartikel, wissenschaftlich - begutachtet (reviewed)
A1  - Gschwind, Larissa
A1  - Jordan, Carmen-Simona
A1  - Vennemann, Norbert
T1  - Devulcanization of ethylene-propylene-diene monomer rubber waste. Effect of diphenyl disulfide derivate as devulcanizing agent on vulcanization, and devulcanization process
JF  - Journal of Applied Polymer Science
N2  - A systematic study was performed to understand the effects of the devulcanizing agent dibenzamido diphenyl disulfide (DBD) on the vulcanization and devulcanization process of a sulfur-cured ethylene-propylene-diene monomer (EPDM) rubber. The influence of DBD on vulcanization was investigated by mixing DBD with virgin rubber and curative system. The devulcanization of rubber waste was achieved with varying amounts of DBD ranging from 0.4 to 13.8 wt% and temperatures from 150 to 200°C. The quality of vulcanizates and devulcanizates was evaluated by rheometer tests, temperature scanning stress relaxation measurements, and analysis of mechanical properties. During vulcanization, DBD acts as an accelerator in the presence of sulfur. When accelerators are added, the scorch time increases, and the cure rate decreases. Thus, DBD acts as a retarder. In the presence of activators, DBD leads to a significant reduction of crosslink density. This results in composites with high elongation at break and poor compression set values. The efficiency of the devulcanization of rubber waste depends strongly on DBD concentration and temperature. The monosulfidic crosslinks are cleaved by low concentrations of DBD, while polysulfidic crosslinks require higher concentrations. These results show that DBD is effective as a devulcanizing agent and degrades the network below 200°C.
Y1  - 2022
UN  - https://nbn-resolving.org/urn:nbn:de:bsz:959-opus-28275
SN  - 1097-4628
SS  - 1097-4628
SN  - 0021-8995
SS  - 0021-8995
U6  - https://doi.org/10.1002/app.52141
DO  - https://doi.org/10.1002/app.52141
VL  - 139
SP  - 16
S1  - 16
ER  -